6-Anilino-1,4,5-trihydroxyanthraquinones

ABSTRACT

Blue anthraquinone dyestuffs are prepared from the reaction of 6-chloro-1,4,5-trihydroxyanthraquinone with an appropriate aniline reactant. The resultant blue dyestuffs are 6-anilino-1,4,5-trihydroxyanthraquinones which produce excellent blue dyeings on polyester fabrics, particularly polyethylene terephthalate.

This is a division, of application Ser. No. 374,772, filed June 28, 1973, now U.S. Pat. No. 3,927,964.

BACKGROUND OF THE INVENTION

Among the polyester fibers, those based on poly(ethylene terephthalate) continue to be the most important, although fibers based on poly(1,4-cyclohexylenemethylene terephthalate) have become commercially available.

Developments in both homo- and copolyesters have continued and many modified versions of polyethylene terephthalate have recently appeared on the market. With the advent of new fibers, the search has continued for dyes which build up on the various types of polyester fabric proportionate to the amount of dye applied, and which are characterized by good light and excellent sublimation properties.

In polyester fibers, the diffusion of the dye into the fiber is effectively controlled by the mobility of the chain molecules in the disordered regions. However, the molecular shape and the size of the dye, the presence of polar groups and general steric considerations are also important in relation to the rate of diffusion.

I have now discovered a new series of anthraquinone dyestuffs producing excellent blue dyeings on polyester fabric materials, in particular, polyethylene terephthalate, and which are also excellent colorants for rigid plastic substrates.

SUMMARY OF THE INVENTION

In accordance with the invention, there is provided aromatic polyester textile material dyed with an anthraquinone dyestuff of the formula: ##SPC1##

Each of R₁ and R₂ is independently hydrogen, chlorine, bromine, alkyl having from 1-8 carbon atoms, alkoxy having from 1-8 carbon atoms, hydroxy(lower alkyl), N-lower alkylamino, N,N-di-lower alkylamino, lower alkoxy lower alkyl, lower alkoxy lower alkoxy and acylamido having up to 7 carbon atoms. The term lower designates an alkyl group having up to 6 carbon atoms, preferably 1-4.

In accordance with a further aspect of the invention, there are provided polyester fabric materials dyed with the above compounds, and, according to a still further preferred embodiment of the invention, there are provided blue rigid plastic materials, the blue color being imparted from the above anthraquinone dyestuffs.

DETAILED DESCRIPTION OF THE INVENTION

The anthraquinone dyestuffs are made in accordance with the following synthetic route: ##SPC2##

In the above synthesis, chrysazin (II) is dichlorinated to produce a 4,x-dichlorochrysazin, which is either a 4,6- or 4,7-dichloro isomer. From analytical studies it is believed that the predominant isomer produced is the 4,7-dichloro isomer, and throughout this application reference will be made to the corresponding products therefrom. 4,7-Dichlorochrysazine is conveniently prepared in accordance with the disclosure in my copending application Ser. No. 253,995, filed May 17, 1972. The 4,7-Dichlorochrysazin is converted into 6-chloro-1,4,5-trihydroxyanthraguinone by hydrolysis, it being discovered that the alpha-chloro group is selectively hydrolyzed leaving the beta-chloro group free for reaction with an appropriate aniline of the formula: ##SPC3##

wherein R₁ and R₂ are as defined above.

I have discovered that certain arylamino trihydroxyanthraquinones provide dyeings of a deep blue hue when applied to polyester textile material by conventional methods. Dyed fabric provided by the invention can be after-treated as required with excellent results. Anilines (V) which may be used to produce dyes of the invention include: aniline; o,m,p-toluidine; the various xylidines; p-aminoacetanilide; N-methyl-p-phenylenediamine; N-butylaniline; p-n-octylaniline; p-t-butylaniline; p-amylaniline; p-n-heptylaniline; 2-[p-(aminoanilino)]ethanol; 2-[p-aminophenyl)]ethanol; 2-(p-aminophenoxyl)ethanol; p-(2-methoxyethoxy)aniline; p-aminopropionanilide; p-aminoatcetophenone and 8-(p-aminophenyl)-n-octanol.

The reaction is conducted in the presence of an alkaline acid-binding agent and a copper salt. Particularly useful acid-binding agents include the alkali metal carbonates, bicarbonates and acetates. Sodium acetate is preferred. The efficiency of the reaction is improved by the presence of a catalytic amount of a copper catalyst, such as copper sulfate or copper acetate.

The reaction mixture is heated to an elevated temperature between 120° C and the reflux temperature of the reaction mixture, usually about 220° C. It is convenient to use an excess of the amine reactant as a reaction medium, although it is possible to use substantially stoichiometric amounts of reactants in the presence of an inert solvent. After completion of the reaction, which generally takes from 4 to 24 hours, the product is separated and recovered by conventional methods.

A particularly convenient way to recover the product in a purified form is to dulute the reaction mixture with methanol or denatured alcohol in an amount of 100 to 300% based on the volume of the reaction mixture. In this method of product recovery, the reaction mixture is first cooled, the alcohol is added and the mixture is reheated to reflux. It is then allowed to cool gradually to room temperature, filtered, and the product collected on the filter is washed again with alcohol and thereafter, oven-dried. When suitable, the alcohol solution of the reaction mixture may be filtered hot.

To prepare the product for application to the polyester substrates the product must be suitably dispersed. This may be done in any of several well-known methods, milling as in a ball-mill with dispersing agents such as lignin sulfonic acid materials, for instance. The resultant aqueous dispersion can be dried, as in a spray-dryer, or preserved and used as a paste. Standardization to any desired lower strength can be done with inert colorless diluents such as inorganic salts for powders, or water for pastes. Other materials such as preservatives, foam-control agents, and wetting agents may be added as desired.

Dispersed pastes are made by wet milling the dye in conventional equipment in the presence of a dispersing agent, preferably sodium lignin sulfonate or sodium alkylnaphthalene sulfonate. Various other commercially available dispersing agents, such as sodium salts of carboxylated polyelectrolytes and the naphthalene sulfonates; e.g., the condensation products of sulfonated naphthalene and formaldehyde, such as sodium dinaphthylmethane disulfonate, are conveniently used. The all disperse paste may be cut or standardized to a standard strength with water. The final color content of the finished paste averages from 10-40 percent by weight (pure color) active dye base.

Disperse powders are prepared by wet milling color in the presence of a dispersant, such as those mentioned hereabove, in equipment such as a ball mill, Werner-Pfleiderer mill or attritor. The dispersed material is oven or spray dried and micropulverized if necessary to provide the dispersed powder. The color is cut or standardized to a standard strength in a blender with a diluent, such as sodium sulfate or dextrin. A wetting agent, such as sodium cetyl sulfate or an alkylphenoxy polyethanol may be added to aid in wetting out the product when it is placed in the dye bath. Disperse powders are usually cut or standardized to 25-60 percent by weight color content (pure color).

The dye, when added to water with or without auxillary agents, forms a near colloidal aqueous dispersion from which the aromatic polyester fiber or textile material is dyed in the conventional manner at 40°-100° C (104°-212° F) to give a colored fiber containing about 0.01-2 percent by weight dye (100% color basis).

Alternatively, dyeing may be accomplished without a carrier at temperatures of 100°-150° C under pressure. Also, the dye may be applied in patterns by conventional printing methods, if desired.

The dye can be also applied to the aromatic polyester fiber by thermofixation methods, such as the "Thermosol" process. This process, which involves padding the cloth with the diluted dye dispersion followed by drying and heating with dried hot air or heated contact rolls, in conveniently used for dyeing polyester fibers and blends containing these fibers. Fixation temperatures of 180°-220° C (356°-428° F) are used for 30 to 90 seconds. If the fabric contains cotton or viscose rayon, apart from synthetic fibers, there is little danger of damaging cellulosic portions, but if wool is present, the temperature must be kept within 180°-200° C and the time must be reduced to 30 seconds.

In order to evaluate the effectiveness of a particular dye for a given type of fiber, the dyed fiber is examined for substantivity of the color, light fastness of the color, and resistance of the color to sublimation and washing. Specific tests for the evaluation of these important properties are described in the examples that follow.

My invention is further illustrated by the following examples:

EXAMPLE 1 6-Anilino-1,4,5-trihydroxyanthraquinone

Charge to a 500 ml. flask equipped with a stirrer, thermometer, heater and an air condenser fitted with a condensate trap,

    ______________________________________                                         150.0  g.       aniline                                                        29.0   g.       6-chloro-1,4,5-trihydroxyanthraquinone                         12.0   g.       sodium acetate (anhydrous) and                                 0.5    g.       cupric acetate.                                                ______________________________________                                    

The charge is stirred and heated for 22 hours at 155° C to 160° C. It is then allowed to cool to 75° C. To the stirred mass is then added

250 ml. ethanol, denatured.

The mass is heated to the boiling temperature (about 80° C) and thenallowed to cool while stirring to room temperature.

The insoluble product is collected on a suction filter and washed with fourportions of denatured ethanol, each

50 ml. ethanol.

The cake is then washed with hot water in portions and sucked as dry as possible on the filter.

A separate dry test indicates that about 30 g. is obtained. The chlorine content of a dried sample of the blue material is less than 0.1%.

To a ball mill is charged the filter cake above, together with

    ______________________________________                                         30     g.      Marasperse CB (a commercially available                                        lignosulfonic acid dispersing agent) and                        200    g.      water (including that which is charged                                         with the wet cake).                                             ______________________________________                                    

Milling is continued until a satisfactory dispersion is obtained as shown by a filter test.

The 6-chloro-1,4,5-trihydroxyanthraquinone used as the starting material may be prepared by dissolving

    ______________________________________                                         21.0   g.       anhydrous boric acid in                                        300.0  g.       sulfuric acid (98%) at 65° C. Then is                                   added                                                          46.5   g.       4,7-dichlorochrysazin.                                         ______________________________________                                    

The temperature is raised to 140° C to 145° C and maintained at that temperature while stirring for 7 hours. The mass is allowed to cool, and drowned into

    ______________________________________                                                1000 g. ice and water.                                                  ______________________________________                                    

The drowning mass is heated to 85° C, stirred briefly and filtered. The cake is washed free of acid with hot water. The dry weight is 43.2 g. The chlorine content is 12.2%; C₁₄ H₇ CIO₅ requires 12.2% Cl.

The resultant 6-chloro-1,4,5-trihydroxyanthraquinone is then suitable for use as the starting material of this example.

EXAMPLE 2

An aqueous dye bath containing 10% Marcron L (a commercially available phenolic dye carrier) and 1 % monosodium phosphate as a buffering agent isprepared. Type 54 "Dacron" polyester fabric is treated in a bath at 120° C for 10 minutes, the fabric-to-water dye bath ratio being 1 :40. The disperse dye made as described in Example 1 is added in an amount sufficient to provide a bath containing 0.4% dye based on the weight of polyester fibers. Dyeing is continued for one hour at 205° F and the fabric is removed from the bath, rinsed and dried. Sample dyeings weretested for sublimation according to standard AATCC Color Fastness to Dry Heat (sublimation) Test No. 117-1967T, Page 123 of the 1970 Technical Manual of the American Association of Textile Chemists and Colorists. Dyedfabric is placed between a sandwich of undyed Dacron polyester fabric and heat is applied for 30 seconds. Sublimation tests were made at 350°F and 400° F on goods as described above. The dyeing was characterized by a clear blue hue. Sublimation tests showed very little transfer of color, even at 400° F.

Similar very good results is obtained when the dye is applied to the fabricby thermofixation methods and then tested for sublimation as described above.

EXAMPLE 3

When 150 g. aniline in Example 1 is replaced by an equimolar amount of p-toluidine, a dye is obtained having the structure: ##SPC4##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

EXAMPLE 4

When 150 g. aniline in Example 1 is replaced by an equimolar amount of p-chloroaniline a dye is obtained having the structure: ##SPC5##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

EXAMPLE 5

When 150 g. aniline in Example 1 was replaced by an equimolar amount of m-aminoacetanilide a dye is obtained having the structure: ##SPC6##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

EXAMPLE 6

When 150 g. aniline in Example 1 is replaced by an equimolar amount of 2-(p-aminophenyl)ethanol a dye is obtained having the structure: ##SPC7##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

EXAMPLE 7

When 150 g. aniline in Example 1 is replaced by an equimolar amount of p-aminoacetophenone a dye is obtained having the structure: ##SPC8##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

EXAMPLE 8

When 150 g. aniline in Example 1 is replaced by an equimolar amount of 2,4-dichloroaniline a dye is obtained having the structure: ##SPC9##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

EXAMPLE 9

When 150 g. aniline in Example 1 was replaced by an equimolar amount of N,N-dimethyl-p-phenylenediamine a dye is obtained having the structure: ##SPC10##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

EXAMPLE 10

When 150 g. aniline in Example 1 is replaced by an equimolar amount of p-tert-butylaniline a dye is obtained having the structure: ##SPC11##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

EXAMPLE 11

When 150 g. aniline in Example 1 is replaced by an equimolar amount of p-(2-methoxyethoxy)aniline a dye is obtained having the structure: ##SPC12##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

EXAMPLE 12

When 150 g. aniline in Example 1 is replaced by an equimolar amount of 2-(p-aminophenoxy)ethanol a dye is obtained having the structure: ##SPC13##

When dispersed and applied to polyester fabric as described in Example 2, the dyeing is characterized by a bright greenish blue hue of good light fastness and very good sublimation. The dyeing also retains its hue under different sources of artificial light.

According to a further aspect of the invention, the dyes of the invention may be used for the coloration of rigid plastic substrates. The rigid plastic substrates contemplated within the scope of the invention are those plastic materials capable of being pigmented with the compounds of the invention, and will be referred to herein as "rigid plastic substrates". The rigid plastic substrates of the invention include those materials capable of being formed into a shaped article, including semi-rigid materials which may be deformed by application of pressure.

As rigid plastic substrates of the invention may be mentioned terpolymers, including acrylonitrile-styrene-butadiene, often known as ABS; acrylics, including methacrylics; polystyrene, both foamed and rubber modified polysulfones; cellulosic derivatives, particularly esters such as cellulose acetate, propionate and butyrate; polyamides such as nylon; epoxy and phenolic resins; polycarbonates; and polyesters. It is understood that the rigid plastic substrates include those materials capable of being pigmented with the compounds of the invention, and therefore copolymers of the above classes of compounds, such as styrene-butadiene, are also within the scope of the invention.

Specific examples of thermoplastic resins include polyvinyl chloride, polyvinyl acetate, vinyl chloride/acetate copolymers, polyvinyl alcohol, polyvinyl acetal, ethylene/vinyl acetate, ethylene/vinyl propionate, ethylene/vinyl isobutyrate, ethylene/vinyl alcohol, ethylene/methyl acrylate, ethylene/ethyl acrylate ethylene/ethyl methacrylate, ethylene/allyl alcohol, ethylene/allyl acetate, ethylene/allyl acetone, ethylene/allyl benzene, ethylene/allyl ether, ethylene/acrolein, polyhexamethylene adipamide, polyhexamethylene sebacamide, polycaprolactam, polymethyl methacrylate, polyacrylonitrile, polymethyl acrylate, polyethyl methacrylate, and styrene/methyl methacrylate.

As preferred rigid plastic substrates of the invention may be mentioned thepolyacrylates, polystyrene and polycarbonates.

The rigid plastic substrates are colored with the compounds of the invention through pigmentation processes. The compounds are admixed with the plastic using sets of mixing rollers, mixing or milling apparatus. After the compounds and the plastic have been thoroughly mixed, the resultant colored mixture is shaped into the desired final form through procedures well known to those skilled in the art, such as pouring, calendering, extrusion, spreading, or injection molding. Where the desiredproduct is a semi-rigid material, plasticizers may advantageously be added prior to shaping into the desired final form. As plasticizers suitable forthis purpose may be mentioned esters of phthalic acid. Although the plasticizer may be incorporated after the mixing of the compound of the invention with the rigid plastic substrate, it also can be incorporated into the rigid plastic material prior to mixing the pigment with the rigidplastic material. In order to vary the strength of the finished product or vary the color, it is also possible to add additional pigments or fillers in an amount sufficient to obtain the desired effect.

The amount of the compound of the invention which is used to color the rigid plastic substrates may vary widely depending upon the degree of color wished to be imparted to the final product, and depending upon whether the compound of the invention is the sole colorant or whether it is used in admixture with other plastic colorants. When the compound of the invention is used in admixture with other colorants, obviously a very minute quantity may be used to produce a complementary effect. Generally, the amount of colorant comprises less than 15%, preferably less than about8%, by weight in relation to the rigid plastic substrate. An amount of colorant compound which has proved particularly valuable is about 0.0001% to about 1%.

EXAMPLE 13

Methylmethacrylate resin is colored with the compound of Example 1 as the colorant, in a ratio of 2 grams resin to 1 mg. colorant. The resin is prepared by placing 1 pound of methylmethacrylate into a Thropp mill (a 2-roller mill), which is than heated and run in order to melt and smash the resin to a molten mass. The compound of Example 1 is added and the entire mixture of resin and colorant is milled until the colorant is uniformly distributed in the mass as measured by eye. While still hot, 30 grams of the hot mass is cut off for use in the following procedure. The sample, containing 30 grams methylmethacrylate and 15 g. of the compound of Example 1 as colorant, may be conveniently molded in a Laboratory 40 Single Acting Watson-Stillman Laboratory Press (Farrell-Birmingham Co. 50-ton press). 30 grams of methylmethacrylate mixture containing 15 mg. ofthe compound of Example 1 per pound of methylmethacrylate is placed in the cold mold, which is then closed with the Schrader Valve. The drain is opened and steam is applied to the mold. When steam comes through the drain pipe, the drain is closed. Up to 25.0 tons pressure is exerted on the chips until the mold is fully closed. This can conveniently be accomplished by observing the pressure gauge. When the gauge needle no longer decreases in pressure, the mold is then closed.

The mold is held closed at zero pressure by releasing the hydraulic pressure and maintaining the steam for 5 minutes. The mold pressure is increased to 10 tons and held for ten minutes, the steam remaining on.

The mold pressure is increased to 15 tons and the steam shut off; the drainis opened and cooling water is added for five minutes. Thereafter the pressure is changed to zero and the mold is opened to extract the resultant plastic chip.

EXAMPLE 14

When the 1 pound of methylmethacrylate are replaced by 2 pounds polystyreneand 10.44 grams titanium dioxide, the procedure of Example 13, being otherwise followed, a fast coloration of the polystyrene is obtained. A clear blue plastic is obtained by omitting the titanium dioxide.

EXAMPLE 15

The compounds of the invention may also be used as colorants for plastics made from polycarbonates. A pigmented plastic material of polycarbonates and the compound of Example 1 may be prepared according to the following procedure:

A specimen is prepared by dry mixing pelletized or powdered resin with finely divided colorant until uniform distribution is achieved of the colorant in the resin material. Plasticizer may also be added, if desired.The mixture is then extruded or injected molded under suitable conditions. 454 gms. Lexan 121-R (General Electric) pellets are placed in Bipel one ounce reciprocating screw injection molder. The pellets are tumbled for 5 minutes on the barrel tumbler. The resin is heated (front zone temperatureof 550° F and rear zone temperature of 500° F) and chips are produced from the virgin resin until chips of good quality are obtained. When the desired quality of chips are obtained with the clear resin, a fresh batch of Lexan 121-R, containing the compound of Example 1 in an equivalent amount corresponding to Example 10 to produce a pigmented plastic material is fed into the injection molder, to produce pigmented chips having excellent fastness characteristics.

EXAMPLE 16

When the compounds of Examples 3-12 are substituted for the compound of Example 1 in the process of Example 13, methylmethacrylate is colored to produce a clear blue shaped plastic material. The compounds of Examples 3-12 may be used to impart coloration to polystyrene following the procedure of Example 14 and polycarbonate is pigmented with the compounds of Examples 3-12 following the procedure of Example 15. 

What is claimed is:
 1. A compound of the formula ##SPC14##each of R₁ and R₂ is independently hydrogen, chlorine, bromine, alkyl having from 1-8 carbon atoms, alkoxy having from 1-8 carbom atoms, hydroxy(lower alkyl), N-lower alkylamino, N,N-di-lower alkylamino, lower alkoxy lower alkyl, lower alkoxy lower alkoxy and acylamido having up to 7 carbon atoms. 